SCM420 alloy steel pipe harden ability is higher, no temper brittleness, weld ability is quite good, form the cold cracking tendency is small, can be good mability and cold plastic strain.

Characteristics and application:

SCM420 seamless pipe in conditioning or carburizing and quenching condition, used in the manufacture of the corrosive medium and working temperature below 250 ℃, the medium containing hydrogen nitrogen mixture work of high pressure pipe and all kinds of fasteners, the more senior carburized parts, such as gear, shaft, etc.

	Chemical composition (%)
C	Si	Mn	P	S	Cr	Mo
0.18-0.23	0.15-0.35	0.60-0.85	0.030max	0.030max	0.90-1.20	0.15-0.30

Yield Strength          Mpa (min)	Tensile  Strength          Mpa(min)	Elogation %(min)
835	685	12

Standard :JIS G 4105

Equivalent material: 20CrMo , 25CrMo4 (1.7218), 40CrNiMoA , 4340 , 817M40 ,816M40

Percentage reduction of area : ≥50

Impact (J/cm2):≥78

Hardness :≤197HB 

Heat treatment  specification :  850 ℃ quenching  ,oil cooling; 500 ℃ tempering, water cooling, oil cooling.

Delivery condition : By heat treatment (normalizing, annealing and high temperature tempering) or heat treatment state delivery, delivery status should be indicated in the contract

SCM420 material under JIS G 4105 standard , this Japanese Industrial Standard specifies chromium molybdenum steels , mainly for machine structural use manufactured by hot forming such as hot rolling and forging ,ordinarily used after further process of forging ,cutting and heat treatment . 

BBN steel specialized in offering SCM420 structural steel pipe for many years , if you have requirement about SCM420 material steel pipe , please contact with us freely .